Material | Polyethylene |
Usage/Application | Corrosion Resistance And Crack |
Size | 1.0 mm |
Color | Black, White, Green, Red , Yellow, Blue, Transparent / Clear |
Roll Length | 200 m |
Packaging Type | Box |
Packaging Size | 16 Rolls |
Shrink Temperature | 90 Degree C |
Temperature Range | 125 Degree C |
Radial Shrinking Ratio | >=50% 2 : 1 |
Longitudinal Change | =<+-5% |
Tensile Strength | >=10.4MPa |
Concentricity | >=65% |
Ultimate Elongation | >=200% |
Aging in Circulating-Air oven | 158.00C +- 1.00C, 168hrs |
After Aging Tensile Strength | >=7.3MPa |
After Aging Ultimate Elongation | >=100% |
Volume Resistivity | >=1014Ohm.cm |
Size |
As supplied(mm.) |
After recovery(mm.) |
||
Inside diameter |
Wall-thickness |
Inside diameter |
Wall-thickness |
|
Φ0.8 |
1.3 ± 0.2 |
0.28 ± 0.08 |
≤0.45 |
0.33 |
Φ1.0 |
1.5 ± 0.2 |
0.20 ± 0.08 |
≤0.6 |
0.33 |
Φ1.5 |
2.0 ± 0.2 |
0.20 ± 0.08 |
≤0.8 |
0.36 |
Φ2.0 |
2.5 ± 0.2 |
0.20 ± 0.09 |
≤1.00 |
0.44 |
Φ2.5 |
3.0 ± 0.2 |
0.25 ± 0.09 |
≤1.25 |
0.44 |
Φ3.0 |
3.5 ± 0.2 |
0.25 ± 0.09 |
≤1.5 |
0.44 |
Φ3.5 |
4.0 ± 0.2 |
0.25 ± 0.3 |
≤1.75 |
0.44 |
Φ4.0 |
4.5 ± 0.2 |
0.25 ± 0.09 |
≤2.0 |
0.44 |
Φ4.5 |
4.8 ± 0.2 |
0.28 ± 0.10 |
≤2.25 |
0.56 |
Φ5.0 |
5.5 ± 0.2 |
0.28 ± 0.10 |
≤2.5 |
0.56 |
Φ6.0 |
6.5 ± 0.2 |
0.28 ± 0.10 |
≤3.0 |
0.56 |
Φ6.5 |
7.0 ± 0.2 |
0.30 ± 0.10 |
≤3.25 |
0.56 |